Poly(tetrafluoroethylene-hexafluoropropylene) films with high energy density and low loss for high-temperature pulse capacitors

Publication date: 7 April 2017
Source:Polymer, Volume 114
Author(s): Xiaomeng Zhang, Yifei Zhao, Yuhao Wu, Zhicheng Zhang
As the most important material of metalized capacitors, dielectric polymers with large energy density (Ue), promising discharging efficiency (η), and elevated breakdown strength (Eb) are dreadfully requested for energy storage purpose. During the charging and discharging circles, the Joule heat could cause significant temperature rising and undesirable early failure in the capacitors. Few of the known polymeric dielectrics are able to work functionally at temperature over 100 °C, especially under high electric field. In present contribution, poly(tetrafluoroethylene-hexafluoropropylene) (P(TFE-HFP)) is fabricated into thin films via hot-pressing followed by uniaxially stretching. At ambient temperature, P(TFE-HFP) films exhibit linear dielectric behaviour like biaxially orientated polypropylene (BOPP). The high Tm and Young's modulus allow P(TFE-HFP) films to work functionally at temperature up to 110 °C, whose Eb is over 500 MV/m, Ue is more than 6 J/cm3 and η is larger than 80%, respectively. The excellent performance suggests that P(TFE-HFP) films may substitute BOPP films to work as dielectric materials at elevated temperature.

Graphical abstract

image


http://ift.tt/2nOKAz4

Δεν υπάρχουν σχόλια:

Δημοσίευση σχολίου

Αναζήτηση αυτού του ιστολογίου