Microstructural evolution, nanoprecipitation behavior and mechanical properties of selective laser melted high-performance grade 300 maraging steel

Publication date: 15 November 2017
Source:Materials & Design, Volume 134
Author(s): Chaolin Tan, Kesong Zhou, Wenyou Ma, Panpan Zhang, Min Liu, Tongchun Kuang
High-performance grade 300 maraging steels were fabricated by selective laser melting (SLM) and different heat treatments were applied for improving their mechanical properties. The microstructural evolutions, nanoprecipitation behaviors and mechanical properties of the as-fabricated and heat-treated SLM parts were carefully characterized and analysed. The evolutions of the massive submicron sized cellular and elongated acicular microstructures are illustrated and theoretically explained. Nanoprecipitates triggered by intrinsic heat treatment and amorphous phases in as-fabricated specimens are observed by TEM. High-resolution TEM (HRTEM) images of the age hardened specimens clearly exhibit massive nanosized needle-shaped nanoprecipitates Ni3X (X=Ti, Al, Mo) and 50–60nm sized spherical core-shell structural nanoparticles embedded in amorphous matrix. XRD analyses reveal austenite reversion and probable phase transformations during heat treatments. The hardness and tensile strength of the as-fabricated and age-treated SLM specimens absolutely meet the standard wrought requirements. Furthermore, the lost ductility after aging can be compensated by preposed solution treatments. Relationships between massive nanoprecipitates and dramatically improved mechanical performances of age hardened specimens are elaborately analysed and perfectly explained by Orowan mechanism. This study demonstrates that high-performance grade 300 maraging steels, which is comparable to the standard wrought levels, can be produced by SLM additive manufacturing.

Graphical abstract

image


http://ift.tt/2uQlJTk

Δεν υπάρχουν σχόλια:

Δημοσίευση σχολίου

Αναζήτηση αυτού του ιστολογίου