Polylactide (PLA) and acrylonitrile butadiene rubber (NBR) blends: The effect of ACN content on morphology, compatibility and mechanical properties

Publication date: 21 April 2017
Source:Polymer, Volume 115
Author(s): Mahshid Maroufkhani, AliAsghar Katbab, Wangcheng Liu, Jinwen Zhang
In this study, attempts have been put to prepare toughened polylactide (PLA) through melt blending with acrylonitrile butadiene rubber (NBR) via melt mixing process. The influences of acrylonitrile (ACN) content on the compatibility, microstructure, tensile properties and impact resistance have been investigated. A matrix-dispersed droplet morphology was noted for all blend samples, and the rubber particle size decreased with decreasing ACN content of NBR. This droplet size, impact strength and elongation all corresponded well to the interfacial interaction that was evidenced by surface tension analysis and melt rheology. It was noted that the interfacial tension decreased with decrease in ACN content, accordingly, the results from both Cole-Cole curves and Han plots indicated high homogeneity of the PLA blend with NBR containing lower ACN contents. On the other hand, all blends exhibited very similar glass transition temperatures and crystallinity. It is concluded that extent of thermodynamic compatibility of PLA and NBR determines the improvement of toughness. Incorporation of only 10 wt% NBR resulted in dramatic improvements of elongation at break and impact strength of PLA and largely retained the high tensile strength of neat PLA.

Graphical abstract

image


http://ift.tt/2mjJuii

Δεν υπάρχουν σχόλια:

Δημοσίευση σχολίου

Αναζήτηση αυτού του ιστολογίου