Effect of incremental equal channel angular pressing (I-ECAP) on the microstructural characteristics and mechanical behaviour of commercially pure titanium

Publication date: 15 May 2017
Source:Materials & Design, Volume 122
Author(s): Muhammad Jawad Qarni, Giribaskar Sivaswamy, Andrzej Rosochowski, Sonia Boczkal
Incremental equal channel angular pressing (I-ECAP) is one of the continuous severe plastic deformation (SPD) processes. This paper presents the processing of commercial purity titanium (CP-Ti) using a double billet variant of I-ECAP process. Ultrafine-grain (UFG) structure was successfully achieved after six passes of I-ECAP at 300°C. Microstructural evolution and texture development were tracked using EBSD. Analysis revealed continuous dynamic recrystallization (CDRX) as one of the grain refinement mechanism during processing. Room temperature tensile tests carried out before and after six passes, shows significant increase in strength with acceptable levels of ductility. The yield strength was increased from 308 to 558MPa and ultimate tensile strength from 549 to 685MPa. Compression tests conducted at different strain rates shows considerable increase in strength and enhanced strain rate sensitivity after processing. A distinct three-stage strain hardening was observed during compression. However the processed material displayed a loss in strain hardening ability during tensile as well as in compression tests. Detailed microhardness measurements show the evolution of hardness after subsequent passes with a reasonable level of homogeneity after the sixth pass. It is demonstrated that I-ECAP is an effective method for grain refinement in CP-Ti and subsequently improving its mechanical properties.

Graphical abstract

http://ift.tt/2nEnCKT