Furan-functionalized aniline trimer based self-healing polymers exhibiting high efficiency of anticorrosion

Publication date: 8 September 2017
Source:Polymer, Volume 125
Author(s): Tsai-Wei Chuo, Ying-Ling Liu
An aniline trimer derivative possessing multiple furan groups (TFAT) is prepared and used as a building unit for preparation of self-healing anticorrosion coatings. The aniline trimer unit brings electrochemical activity to TFAT, and the tertiary amine and glycidylether groups provide TFAT excellent adhesive ability. Both features contribute to the high performance of anticorrosion property of crosslinked TFAT coatings on cold-rolled steel (CRS). An ultralow corrosion rate of 0.12 μm y−1 and a high impedance at low frequency (Z0) of 9.2 × 105 Ω cm−2 have been recorded with the coatings, both demonstrate hundreds times enhancements of the anticorrosion properties compared to the CRS samples coated with crosslinked aniline trimer (corrosion rate: 71 μm y−1; Z0: 1240 Ω cm−2). Moreover, as possessing furan groups, TFAT is a suitable agent to react with multifunctional maleimide compounds for formation of thermally-reversible crosslinked networks through Diels-Alder reaction. Consequently, TFAT-based self-healing anticorrosion coatings are obtained. In a cycle test, the TFAT-based reversible crosslinked coating demonstrates a high self-healing efficiency of anticorrosion with a recovery of protection efficiency from 79.8% to 99.2%, corresponding to a 99.3% of protection efficiency based recovery. A new material showing high anticorrosion and self-healing efficiency for self-healing anticorrosion coatings has been demonstrated.

Graphical abstract

image


http://ift.tt/2w0eetn

Δεν υπάρχουν σχόλια:

Δημοσίευση σχολίου

Αναζήτηση αυτού του ιστολογίου