Interfacial microstructures and mechanical properties of Mg/Al bimetal produced by a novel liquid-liquid compound casting process

Publication date: November 2018
Source:Journal of Materials Processing Technology, Volume 261
Author(s): Zailiang Jiang, Zitian Fan, Wenming Jiang, Guangyu Li, Yao Wu, Feng Guan, Haixiao Jiang
In the present work, a novel method was proposed to produce Mg/Al bimetal using the lost foam casting (LFC) liquid-liquid compound process with a Zn interlayer, and the interfacial microstructures and mechanical properties of the Mg/Al bimetal were investigated for the first time. Obtained results reveal that a compact metallurgical interface was formed between the AZ91D magnesium alloy substrate and the A356 aluminum alloy substrate. The metallurgical interface included two reaction layers. The reaction layer adjacent to the AZ91D substrate was composed of α-Mg, Al5Mg11Zn4 and MgZn phases, and the reaction layer adjacent to the A356 substrate consisted of α-Al, Mg32(Al, Zn)49 and Mg2Si phases. The addition of the Zn interlayer not only prevented different liquid metals from directly mixing, but also restrained the formation of Mg-Al intermetallics. The microhardnesses of the reaction layers were much higher than those of the substrates, and the reaction layer close to the A356 substrate had the highest microhardness. The shear strength of the Mg/Al bimetal was about 10.91 MPa, and the fracture surface of the Mg/Al bimetal exhibited a brittle fracture nature.

Graphical abstract

image


https://ift.tt/2t0yzeM

Δεν υπάρχουν σχόλια:

Δημοσίευση σχολίου

Αναζήτηση αυτού του ιστολογίου