Modeling of bake-hardening effect for fine grain bainite-aided dual phase steel

Publication date: 15 March 2017
Source:Materials & Design, Volume 118
Author(s): N. Ormsuptave, V. Uthaisangsuk
Bake hardening (BH) effects of dual phase (DP) steels with consideration of grain size and bainitic phase were investigated. Basically, after BH process, DP steels exhibited complex microstructure characteristic including Cottrell atmosphere, precipitation in ferrite and tempered martensite. Firstly, severe plastic deformation, namely, constrained groove pressing (CGP) was applied to a ferrite–pearlite low carbon steel for producing fine grain microstructure with submicron size. Subsequently, DP steel and DP steel with bainite were generated by intercritical annealing following by water and oil quenching, respectively. The BH at the temperature of 160°C for 20min was performed for steel samples with different microstructures after pre-straining to 2, 6 and 10%. Obviously, fine grain structure and bainite could effectively increase the bake hardenability of the examined steels. Additionally, micromechanics based modeling for describing flow stress behavior of the DP steels after BH was done. Hereby, influences of carbon accumulation, occurred carbides and softened martensite were incorporated. Accordingly, the flow curves of the investigated DP steels before and after BH were fairly predicted by means of representative volume element (RVE) finite element (FE) simulations. The increased yield strengths, BH values and resulting strain hardening curves could be accurately described.

Graphical abstract

http://ift.tt/2j18idh