Sulfidation behavior and mechanism of zinc silicate roasted with pyrite

Publication date: 30 March 2018
Source:Applied Surface Science, Volume 435
Author(s): Yong Ke, Ning Peng, Ke Xue, Xiaobo Min, Liyuan Chai, Qinglin Pan, Yanjie Liang, Ruiyang Xiao, Yunyan Wang, Chongjian Tang, Hui Liu
Sulfidation roasting followed by flotation is widely known as a possible generic technology for enriching valuable metals in low-grade Zn-Pb oxide ores. Zn2SiO4 is the primary Zn phase in willemite. Zn4Si2O7(OH)2(H2O), the main Zn phase in hemimorphite, transforms into Zn2SiO4 at temperatures above 600 °C. To enrich the Zn in willemite and hemimorphite, the Zn species should first be converted to ZnS. Therefore, a thorough understanding of the sulfidation reaction of Zn2SiO4 during roasting with pyrite is of vital important. In this study, the sulfidation behavior and reaction mechanisms of a Zn2SiO4-pyrite roasting system were determined using HSC 5.0 software, TG-FTIR spectroscopy, XRD, XPS and SEM-EDS. The results indicate that the sulfidation process can be divided into three steps: the decomposition of pyrite and formation of a sulfur-rich environment, the sulfur-induced migration of O²⁻ and transformation of sulfur vapor, and the sulfidation reaction via oxygen-sulfur exchange. During the sulfidation roasting process, pyrite was converted to loose and porous Fe3O4, whereas Zn2SiO4 was transformed into ZnS and SiO2 in situ. These findings provide theoretical support for controlling the sulfidation roasting process of willemite and hemimorphite.

Graphical abstract

http://ift.tt/2o1oVIP